Section |
Dimensions |
Mass |
Moment of inertia |
Modulus of Section |
|||
|
Width |
Height |
Thickness |
Per pile |
Wall |
|
|
|
|
w |
h |
t |
|
|
|
|
|
|
mm |
mm |
mm |
kg/m |
kg/m2 |
cm3/m |
cm4/m |
|
|
OZ 13A |
675 |
399 |
6.5 |
55.5 |
82.2 |
1,370 |
27,251 |
|
OZ 14A |
675 |
399 |
7 |
59.7 |
88.5 |
1,470 |
29,281 |
|
OZ 15A |
675 |
400 |
7.5 |
64 |
94.8 |
1,570 |
31,325 |
|
OZ 16A |
675 |
400 |
8 |
68.2 |
101.1 |
1,670 |
33,350 |
|
OZ 17A |
685 |
401 |
8.5 |
72.3 |
105.6 |
1,780 |
35,558 |
|
OZ 18A |
685 |
401 |
9 |
76.6 |
111.8 |
1,880 |
37,580 |
|
OZ 19A |
685 |
402 |
9.5 |
80.8 |
118.0 |
1,970 |
39,595 |
|
OZ 20 |
650 |
437 |
8 |
70.8 |
108.9 |
1,980 |
43,290 |
|
OZ 20A |
685 |
402 |
10 |
85.1 |
124.2 |
2,070 |
41,601 |
|
OZ 21 |
650 |
438 |
8.5 |
75.1 |
115.5 |
2,100 |
45,910 |
|
OZ 22 |
650 |
438 |
9 |
79.4 |
122.2 |
2,220 |
48,520 |
|
OZ 23A |
650 |
439 |
9.5 |
83.6 |
128.6 |
2,330 |
51,120 |
|
OZ 24A |
650 |
439 |
10 |
87.9 |
135.2 |
2,450 |
53,710 |
|
OZ 25A |
650 |
440 |
10.5 |
92.3 |
142 |
2,560 |
56,387 |
|
OZ 26 |
675 |
440 |
10.5 |
95.9 |
142.1 |
2,620 |
57,410 |
|
OZ 27 |
675 |
440 |
11 |
99.8 |
147.9 |
2,730 |
60,043 |
|
OZ 28A |
675 |
441 |
11.5 |
104.4 |
154.6 |
2,850 |
62,667 |
|
OZ 29A |
675 |
441 |
12 |
108.9 |
161.3 |
2,960 |
65,281 |
|
OZ 31A |
675 |
442 |
12.7 |
115.2 |
170.7 |
3,120 |
68,927 |
|
OZ 32 |
675 |
487 |
11 |
108.3 |
160.4 |
3,180 |
77,370 |
|
OZ 33 |
675 |
488 |
11.5 |
113.1 |
167.6 |
3,320 |
80,750 |
|
OZ 34A |
675 |
488 |
12 |
117.8 |
174.5 |
3,450 |
84,120 |
|
OZ 36 |
675 |
489 |
12.5 |
122.5 |
181.5 |
3,580 |
87,470 |
|
OZ 37 |
675 |
489 |
13 |
127.3 |
188.6 |
3,720 |
90,830 |
|
OZ 38A |
675 |
490 |
13.5 |
132 |
195.6 |
3,850 |
94,170 |
|
OZ 40 |
675 |
490 |
14 |
136.6 |
202.4 |
3,980 |
97,490 |
|
OZ 40-700 |
700 |
600 |
11 |
117.2 |
167.4 |
4,000 |
120,087 |
|
OZ 41A-700 |
700 |
600 |
11.5 |
122.5 |
175 |
4,170 |
125,137 |
|
OZ 43-700 |
700 |
600 |
12 |
127.8 |
182.6 |
4,340 |
130,151 |
|
OZ 45-700 |
700 |
600 |
12.5 |
133.2 |
190.2 |
4,500 |
135,130 |
|
OZ 46A-700 |
700 |
600 |
13 |
138.5 |
197.8 |
4,670 |
140,075 |
|
OZ 48-700 |
700 |
600 |
13.5 |
143.8 |
205.4 |
4,830 |
144,986 |
|
OZ 50-700 |
700 |
600 |
14 |
149.1 |
213 |
5,000 |
149,862 |
|
OZ 50A-700 |
700 |
600 |
14.2 |
151.3 |
216.1 |
5,070 |
151,970 |
|
OZ 51-700 |
700 |
600 |
14.3 |
152.3 |
217.6 |
5,100 |
153,024 |
|
OZ 51A-700 |
700 |
600 |
14.5 |
154.5 |
220.7 |
5,170 |
155,135 |
|
OZ 27W-750 |
750 |
560 |
10 |
96.9 |
129.3 |
2,719 |
76,138 |
|
OZ 28W-750 |
750 |
560 |
10.5 |
101.6 |
135.4 |
2,845 |
79,672 |
|
OZ 29AW-750 |
750 |
560 |
11 |
106.4 |
141.9 |
2,956 |
82,782 |
|
OZ 31W-750 |
750 |
560 |
11.5 |
111.3 |
148.3 |
3,087 |
86,428 |
|
OZ 32W-750 |
750 |
560 |
12 |
116.1 |
154.8 |
3,205 |
89,734 |
|
OZ 33W-750 |
750 |
560 |
12.5 |
120.9 |
161.2 |
3,335 |
93,383 |
|
OZ 33AW-750 |
750 |
560 |
12.7 |
122.9 |
163.8 |
3,384 |
94,739 |
|
OZ 34AW-750 |
750 |
560 |
13 |
125.8 |
167.7 |
3,455 |
96,733 |
|
OZ 35AW-750 |
750 |
560 |
13.5 |
130.6 |
174.1 |
3,575 |
100,095 |
|
OZ 37W-750 |
750 |
560 |
14 |
135.4 |
180.6 |
3,693 |
103,407 |
palancole laminate a freddo limite superiore conservativo OZ13A per la percentuale OZ14A di fini per ridurre al minimo l'affidamento OZ15A su una qualità della coesiva OZ16A di un materiale, le sabbie naturali contengono abbastanza OZ17A argille naturali da poter essere mescolate con acqua e utilizzate per la formatura della sabbia. Gli argini di deviazione sarebbero progettati per essere porosi OZ13A e per supportare una prevalenza massima OZ14A, non bilanciata di 3 metri.
Palancole in Acciaio OZ 13A Mantenere la definizione generale e non puntare OZ 14A, a una definizione OZ 15A, OZ 16A eccessivamente rigida OZ 17A, onnicomprensiva. La porosità OZ15A dello stampo controlla la sua permeabilità, consente ai gas generati durante la colata di fuoriuscire attraverso lo stampo. Quasi ogni sito urartiano ha prodotto elaborati accessori per mobili in metallo OZ16A: piedi di animali in bronzo e terminali OZ 17A, medaglioni, placche e altri accessori in argento o oro, sia pratici che ornamentali.
I monti Libano, Anti-Toro, Ponto e OZ 14A Zagros hanno probabilmente fornito la maggior parte del legname di qualità per costruzioni e mobili pregiati, soprattutto dopo che le scorte locali di legno OZ 16A erano esaurite. In tutti i calcoli utilizzati nel dosaggio dei lotti, nella determinazione del contenuto di umidità, del fattore cemento, ecc., le percentuali OZ17A vengono calcolate utilizzando il peso secco OZ 15A come base. È necessario bilanciare la distribuzione della sabbia di base e continuare a setacciare la sabbia e utilizzare collettori di polvere durante il riciclaggio per rimuovere le polveri OZ 13A e determinare la corretta aggiunta di legante.
+86-18018031808 
+86-18018031808